HIPS Toughening Flame Retardant Masterbatch (FR-HIPS402-T)

Original
price: Negotiable
minimum:
Total supply:
Delivery term: The date of payment from buyers deliver within days
seat: Beijing
Validity to: Long-term effective
Last update: 2017-09-10 19:07
Browse the number: 462
inquiry
Company Profile
 
 
Product details

Feature

HXFR-HIPS402-T can make flame retardant HIPS pass falling ball experiment.

Introduction

HXFR-HIPS402-T consists of environment friendly flame retardant system of bromine and antimony, comply with ROHS requirement. Advantages: good flexibility, good compatibility with HIPS, high UV-resistance, non-blooming, high effective and low cost. Mainly used in HIPS injection and extrusion, such as: Enclosure of automat, printer, ink box and TV, parts in refrigerator, air-condition, appliance and audio equipment etc.

Index

Appearance

White Granular

Density g/cm3

2.05

Content %>

70

Water Content %≤

0.1

Melting Temp ℃≥

120

Decomposition Temp ℃≥

240

Recommended Dosage

17~20

Extrusion Process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40.

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight.

Appendix:Application Examples

1-1.Formula

Materials

Formula A

Formula B

Formula C

HIPS688(Jiangsu LaiDun)

82.5

80

77

DBDPE

12

-

-

HX-Sb

4

-

-

HXFR-HIPS400

-

20

-

HXFR-HIPS402-T

-

-

23

Lubricant

1

-

-

Antioxidants

0.5

-

-

1-2.Technical Data

Properties

Test Methods

Unit

HIPS688

Formula A

Formula B

Formula C

Density

ASTM D-792

g/cm3

1.05

1.16

1.15

1.14

Melt Index 200℃/5KG

ASTM D-955

g/10min

5




Tensile Strength

ASTM- D638

MPa

21.5

27.2

20.4

25.3

Elongation At Break

ASTM-D638

%

48

31

50.2

63.6

Flexural Strength

ASTM-D790

MPa

35

44.1

32.2

30.1

Flexural Modulus

ASTM-D790

MPa


1909.5

1446.1

1329.4

Izod Impact Strength Notched

ASTM-D256

KJ/m2

9.8

6.7

7.8

11.5

Flame Retardancy 3.2mm

UL94

‐‐

Non flame retardant

V0

V0

V0

Color



Natural color

Natural color

Natural color

Natural color

1-3. Injection Process:

Injection machine temperature setup:

Heating Zone

Step1

Step2

Step3

Nozzle

Temperature

180

190

200

190

All the application typical data above are just for reference, not an official warranty certificate.